Rhenium

From Wikipedia, the free encyclopedia

Jump to: navigation, search
75 tungstenrheniumosmium
Tc

Re

Bh
Periodic Table - Extended Periodic Table
General
Name, Symbol, Number rhenium, Re, 75
Chemical series transition metals
Group, Period, Block 7, 6, d
Appearance grayish white
Standard atomic weight 186.207(1)  g·mol−1
Electron configuration [Xe] 4f14 5d5 6s2
Electrons per shell 2, 8, 18, 32, 13, 2
Physical properties
Phase solid
Density (near r.t.) 21.02  g·cm−3
Liquid density at m.p. 18.9  g·cm−3
Melting point 3459 K
(3186 °C, 5767 °F)
Boiling point 5869 K
(5596 °C, 10105 °F)
Heat of fusion 60.43  kJ·mol−1
Heat of vaporization 704  kJ·mol−1
Heat capacity (25 °C) 25.48  J·mol−1·K−1
Vapor pressure
P(Pa) 1 10 100 1 k 10 k 100 k
at T(K) 3303 3614 4009 4500 5127 5954
Atomic properties
Crystal structure hexagonal
Oxidation states 7, 6, 5, 4, 3, 2, 1, −1, −2, −3
(mildly acidic oxide)
Electronegativity 1.9 (scale Pauling)
Ionization energies
(more)
1st:  760  kJ·mol−1
2nd:  1260  kJ·mol−1
3rd:  2510  kJ·mol−1
Atomic radius 135  pm
Atomic radius (calc.) 188  pm
Covalent radius 159  pm
Miscellaneous
Magnetic ordering  ?
Electrical resistivity (20 °C) 193 n Ω·m
Thermal conductivity (300 K) 48.0  W·m−1·K−1
Thermal expansion (25 °C) 6.2  µm·m−1·K−1
Speed of sound (thin rod) (20 °C) 4700 m/s
Young's modulus 463  GPa
Shear modulus 178  GPa
Bulk modulus 370  GPa
Poisson ratio 0.30
Mohs hardness 7.0
Vickers hardness 2450  MPa
Brinell hardness 1320  MPa
CAS registry number 7440-15-5
Selected isotopes
Main article: Isotopes of rhenium
iso NA half-life DM DE (MeV) DP
185Re 37.4% Re is stable with 110 neutrons
187Re 62.6% 4.35×1010 y α 1.653 183Ta
β- 0.003 187Os
References

Rhenium (IPA: /ˈɹiːniəm/) is a chemical element in the periodic table that has the symbol Re and atomic number 75. A silvery-white, rare, heavy, polyvalent transition metal, rhenium resembles manganese chemically and is used in some alloys. Rhenium is obtained as a by-product of molybdenum refinement and rhenium-molybdenum alloys are superconducting. This was the last naturally-occurring element to be discovered and belongs to the ten most expensive metals on Earth (over US$ 4000.-/kg).

Contents

  • 1 Notable characteristics
  • 2 Applications
  • 3 History
  • 4 Occurrence
  • 5 Isotopes
  • 6 Precautions
  • 7 See also
  • 8 References
  • 9 External links

[edit] Notable characteristics

Rhenium is a silvery white metal, lustrous, and has one of the highest melting points of all elements, exceeded by only tungsten and carbon. It is also one of the most dense, exceeded only by platinum, iridium, and osmium. Rhenium has the widest range of oxidation states of any known element: -3,-1,+1,+2,+3,+4,+5,+6 and +7. The oxidation states +7,+6,+4,+2 and -1 are the most common.

Its usual commercial form is a powder, but this element can be consolidated by pressing and resistance-sintering in a vacuum or hydrogen atmosphere. This procedure yields a compact shape that is in excess of 90 percent of the density of the metal. When annealed this metal is very ductile and can be bent, coiled, or rolled. Rhenium-molybdenum alloys are superconductive at 10 K; tungsten-rhenium alloys are also superconductive, around 4-8 K depending on the alloy.[citation needed]

[edit] Applications

This element is used in platinum-rhenium catalysts which in turn are primarily used in making lead-free, high-octane gasoline and in high-temperature superalloys that are used to make jet engine parts. Other uses:

[edit] History

Rhenium (Latin Rhenus meaning "Rhine") was the next-to-last naturally occurring element to be discovered. The existence of a yet undiscovered element at this position in the periodic table had been predicted by Henry Moseley in 1914. It is generally considered to have been discovered by Walter Noddack, Ida Tacke, and Otto Berg in Germany. In 1925 they reported that they detected the element in platinum ore and in the mineral columbite. They also found rhenium in gadolinite and molybdenite. In 1928 they were able to extract 1 g of the element by processing 660 kg of molybdenite.

The process was so complicated and the cost so high that production was discontinued until early 1950 when tungsten-rhenium and molybdenum-rhenium alloys were prepared. These alloys found important applications in industry that resulted in a great demand for the rhenium produced from the molybdenite fraction of porphyry copper ores.

In 1908, Japanese chemist Masataka Ogawa announced that he discovered the 43rd element, and named it nipponium (Np) after Japan (which is Nippon in Japanese). However, later analysis indicated the presence of rhenium (element 75), not element 43. The symbol Np was later used for the element neptunium.

[edit] Occurrence

Rhenium is not found free in nature, and it was only recently that the first rhenium mineral was found. In 1994, Nature published a letter describing a rhenium sulfide mineral found condensing from a fumarole on Russia's Kudriavy volcano.[3] This is not an economically viable source of the element. Rhenium is widely spread through the Earth's crust at approximately 1 ppb.

Commercial rhenium is extracted from molybdenum roaster-flue gas obtained from copper-sulfide ores. Some molybdenum ores contain 0.002% to 0.2% rhenium. Total world production is between 40 and 50 tons/year; the main producers are in Chile, USA and Kazakhstan. Recycling of used Pt-Re catalyst and special alloys allow the recovery of another 10 tons/year.

The metal form is prepared by reducing ammonium perrhenate with hydrogen at high temperatures.

[edit] Isotopes

Main article: Isotopes of rhenium

Naturally occurring rhenium is 37.4% 185Re, which is stable, and 62.6% 187Re, which is unstable but has a very long half-life. There are twenty-six other unstable isotopes recognized.

[edit] Precautions

Little is known about rhenium toxicity so it should be handled with care.